The ammonia slip catalyst (ASC), typically composed of Pt oxidation catalyst overlaid with SCR catalyst, is employed for the mitigation of NH3 slip originating from SCR catalysts. Oxidation and SCR functionalities in an ASC can degrade through two key mechanisms i) irreversible degradation due to thermal aging and ii) reversible degradation caused by sulfur-oxides. The impact of thermal aging is well understood and it mainly degrades the SCR function of the ASC and increases the NH3 conversion to undesired products [1]. This paper describes the impact of sulfur-oxides on critical functions of ASC and on NH3 oxidation activity and selectivity towards N2, NOx and N2O. Furthermore impact of desulfation under selected conditions and its extent of ASC performance recovery is explained.

Typical Lean NOx Trap (LNT) catalyst composition includes precious metal components (Pt, Pd, and/or Rh), responsible for NO oxidation during lean operation and NOx reduction during rich operation. It was found that redox history of commercial LNT catalyst plays a significant role on deciding its NOx conversion under Lean/Rich cyclic condition. Further test had shown that fully formulated LNT catalyst being pre-reduced had shown much better NO reduction activity during the temperature-programmed reduction (TPRx) of NO than the same LNT catalyst being oxidized. The following study with Rh-only and Pt-only catalyst had demonstrated that Rh plays a key role on the large variation of the NO reduction function due to oxidation state change over LNT catalyst.

Despite drastic reduction of sulfur content in diesel fuel in the recent years, especially with the introduction of Ultra-Low Sulfur Diesel (ULSD), sulfur poisoning remains one of the most significant factors impacting performance of various catalysts in diesel aftertreatment systems. This is because even with ULSD, cumulative exposure of a catalyst over its lifetime in a heavy-duty diesel system may amount to kilograms of sulfur. In this study, we have found that the impact of sulfur poisoning on the performance of various diesel oxidation catalysts (DOC) strongly depends on the catalyst's operation history. For example, exposing a DOC to limited amounts of freshly deposited sulfur in bench reactor testing was shown to have a substantial detrimental effect. On the other hand, several samples which returned from vehicle or test-cell aging with high sulfur loading, have shown no signs of poisoning.

Stoichiometric natural gas engines with three-way catalysts emit less NOx and CH4 due to their higher efficiency compared to lean-burn natural gas engines. Although hydrothermal aging of three-way catalysts has been extensively studied, a deeper understanding beyond hydrothermal aging is needed to explain real-world performance, especially for natural gas engines with near-zero NOx emissions. In this investigation, field-aged three-way catalysts were characterized to identify the contribution of chemical aging to their overall performance. It was found that the sulfur species on the field-aged TWCs were entirely distributed along the catalyst length, showing a decreasing trend, whereas phosphorous contamination was mainly observed at the inlet section of the three-way catalysts, and the phosphorous concentration declined sharply along the axial length.

Exposure of hydrocarbons (HCs) and particulate matter (PM) under certain real-world operating conditions leads to carbonaceous deposit formation on V-SCR catalysts and causes reversible degradation of its NOx conversion. In addition, uncontrolled oxidation of such carbonaceous deposits can also cause the exotherm that can irreversibly degrade V-SCR catalyst performance. Therefore carbonaceous deposit mitigation strategies, based on their characterization, are needed to minimize their impact on performance. The nature and the amount of the deposits, formed upon exposure to real-world conditions, were primarily carried out by the controlled oxidation of the deposits to classify these carbonaceous deposits into three major classes of species: i) HCs, ii) coke, and iii) soot. The reversible NOx conversion degradation can be largely correlated to coke, a major constituent of the deposit, and to soot which causes face-plugging that leads to decreased catalyst accessibility.

This paper presents an extension of our earlier work on Cummins Vehicle Mission Simulation (VMS) software. Previously, we presented VMS as a Windows based analysis tool to simulate vehicle missions quickly and to gauge, communicate, and improve the value proposition of Cummins engines to customers. We have subsequently extended this VMS architecture to build a grid-computing platform to support high volume of simulation needs. The building block of the grid-computing version of VMS is an executable file that consists of vehicle and engine simulation models compiled using Real Time Workshop. This executable file integrates MATLAB and Simulink with Java, XML, and JDBC technologies and interacts with the MySQL database. Our grid consists of a cluster of twenty Linux servers with quad-core processors. The Sun Grid Engine software suite that administers this cluster can batch-queue and execute 80 simulations concurrently.

The measurement of solid particles down to 10 nm is being incorporated into global technical regulations (GTR). This study explores the measurement of solid particles below 23 nm by using both current and proposed particle number (PN) systems having different volatile particle remover (VPR) methodologies and condensation particle counter (CPC) cutoff diameters. The measurements were conducted in dynamometer test cells using ten diesel and eight natural gas (NG) engines that were going under development for a variety of global emission standards. The PN systems measured solid PN from more than 700 test cycles. The results from the preliminary campaign showed a 10-280% increase in PN emissions with the inclusion of particles below 23 nm.

The development and release process for Cummins first US HD OBD certified product encountered numerous hurdles. Beyond the purely "technical" difficulties, there were also challenges related to our product development processes. This presentation provides recommendations for HD OBD product development processes & improvements. Topics will include: Training needs for program management, Performance tuning strategies vs. OBD needs, Planning for post-certification product changes, etc. Presenter Greg Moore, Cummins Inc.

In recent years, the focus on engine parasitic losses has increased as a result of the efforts to increase engine efficiency and reduce greenhouse gasses. The engine gear train, used to time the valve system and drive auxiliary loads, contributes to the overall engine parasitic losses. Anti-backlash gears are often used in engine gear trains to reduce gear rattle noise resulting from the torsional excitation of the gear train by the engine output torque. Friction between sliding surfaces at the gear tooth is a major source of power loss in gear trains. The effect of using anti-backlash gears on the gear friction power loss is not well known. As a part of the effort to reduce parasitic losses, the increase in friction power loss in the Cummins ISX 15 gear train due to the anti-backlash gear was quantitatively determined by modifying the methods given in ISO 14179-2 to fit the anti-backlash gear sub-assembly.

Traditionally, most charge air coolers (CACs) have been constructed using the Nocolok aluminum brazing process. The Nocolok process uses flux, some of which remains after the manufacturing process, and migrates through the intake tract to the engine during normal use. This migration and deposition on engine components can cause a variety of issues with engine operation. Currently the only alternative to Nocolok brazed CACs for engines sensitive to flux migration is vacuum brazing, which comes at a significant price increase. In the effort to reduce cost and increase efficiency, there is interest in whether a Nocolok brazed CAC with a reduced amount of flux residue can be successfully applied to flux-sensitive engines.

Good understanding and accurate prediction of component fatigue strength is crucial in the development of modern engine. In this paper a detail analysis was conducted on an engine component made of gray cast iron with finite element method to evaluate the fatigue strength. This component has notches that cause local stress concentration. It is well known that fatigue behavior of a notch is not uniquely defined by the local maximum stress but depends on other factors determined by notch geometry and local stress distribution. The component fatigue strength was underestimated by only considering the stresses on the notch surface for fatigue life prediction. The critical distance approach was adopted to predict the fatigue behavior of this component. Good agreements are observed between predicted life by the critical distance method and actual field data.

The prediction accuracy of a three-way catalyst (TWC) model is highly associated with the ability of the model to incorporate the reaction kinetics of the emission process as a lambda function. In this study, we investigated the O2 and H2 concentration profiles of TWC reactions and used them as critical inputs for the development of a global TWC model. We presented the experimental data and global kinetic model showing the impact of thermal degradation on the performance of the TWC. The performance metrics investigated in this study included CH4, NOx, and CO conversions under lean, rich, and dithering light-off conditions to determine the kinetics of oxidation reactions and reduction/reforming/water-gas shift reactions as a function of thermal aging. The O2 and H2 concentrations were measured using mass spectrometry to track the change in the oxidation state of the catalyst and to determine the mechanism of the reactions under these light-off conditions.

The aging impact on oxygen storage capacity (OSC) and catalyst performance was investigated on one degreened and one aged (hydrothermally aged at 955 °C for 50 h) commercial three-way catalyst (TWC) by experiments and modeling. The difference of OSC between the degreened and aged TWCs was dependent on catalyst temperature. The largest difference was found at 600 °C, at which the amount of OSC decreased by 45.5%. Catalyst performance was evaluated through lightoff tests at two simulated engine exhaust conditions (lean and rich) on a micro-reactor. The aging impact on the catalyst performance was different under lean and rich environments and investigated separately. At the lean condition, oxidation of CO and C3H6 was significantly suppressed while oxidation of C3H8 was relatively less degraded. At the rich condition, the inhibition effect was more pronounced on the aged TWC and inhibiting hydrocarbon species from C3H6 partial oxidation can survive at temperatures up to 450 °C.

Due to increasing expectations for gasoline like sound quality, today's diesel engines for light and medium duty automotive markets needs to be carefully designed from NVH perspective. Typical engine operating conditions such as low idle, light tip in, tip out demand more attention as they are more prone to generating sound quality concerns. Any abrupt change in the noise signature may be perceived as a sign of malfunction and could have a potential to generate warranty claims. In this paper, an experimental investigation was carried out to determine the root cause of the transient oil pressure regulator buzz noise which occurred during no load transients at low engine speeds. The root cause of the objectionable noise was found to be associated with the impacts of the regulator plunger on the valve seat at certain engine speeds. Noise and vibration diagnostic tests confirmed that the plunger impacts at the seat caused the objectionable buzz noise.

Effects of methyl ester biodiesel fuel blends on NOx emissions are studied experimentally and analytically. A precisely controlled single cylinder diesel engine experiment was conducted to determine the impact of a 20% blend of soy methyl ester biodiesel (B20) on NOx emissions. The data were then used to calibrate KIVA chemical kinetics models which were used to determine how the biodiesel blend affects NOx production during the combustion process. In addition, the impact on the engine control system of the lower specific energy content of biodiesel was determined. Both factors, combustion and controls, must be taken into account when determining the net NOx effect of biodiesel compared to conventional diesel fuel. Because the magnitude and even direction of NOx effect changes with engine load, the NOx effect associated with burning biodiesel blends over a duty cycle depends on the duty cycle average power and fuel cetane number.

Copper- and Iron- based metal-zeolite SCR catalysts are widely used in US and European diesel aftertreatment systems to achieve drastic reduction in NOx emission. These catalysts are highly selective to N2 under wide range of operating conditions. Nevertheless, the type of transition metal has a significant impact on the key performance and durability parameters such as NOx conversion, selectivity towards N2O, hydrothermal stability, and sensitivity to fuel sulfur content. In this study, we explained the differences in the performance characteristics of these catalysts based on their relative acidic-basic nature of transition metal present in these catalysts using practically relevant gas species present in diesel exhaust such as NO2, SOx, and NH3. These experiments show that Fe-zeolite has relatively acidic nature as compared to Cu-zeolite that causes NH3 inhibition and hence explains low NOx conversion on Fe-zeolite at low temperature under standard SCR conditions.

Heat rejection, liner temperature, exhaust valve seat temperature, and head gasket temperature data were recorded during a full load torque sweep of a compression ignition engine when fueled by No. 2 diesel and an ethanol/diesel fuel blend containing 10% ethanol by volume. Heat balances were calculated for engine operation at various load-speed combinations. The results of this study indicated that a greater than expected volume of E-diesel was required to operate the compression ignition engine at the same torque-speed compared to No. 2 diesel. More E-diesel fuel was required due to lower brake thermal efficiencies for E-diesel. Other than exhaust seat temperatures, there were no appreciable differences in component temperatures measured throughout the engine or the results of the heat balances calculated for the No. 2 diesel and E-diesel fuels.

Dynamometer (dyno) durability testing plays a significant role in reliability and durability assessment of commercial engines. Frequently, durability test procedures are based on warranty history and corresponding component failure modes. Evolution of engine designs, operating conditions, electronic control features, and diagnostic limits have created challenges to historical-based testing approaches. A physics-based methodology, known as Load Matrix, is described to counteract these challenges. The technique, developed by AVL, is based on damage factor models for subsystem and component failure modes (e.g. fatigue, wear, degradation, deposits) and knowledge of customer duty cycles. By correlating dyno test to field conditions in quantifiable terms, such as customer equivalent miles, more effective and efficient durability test suites and test procedures can be utilized. To this end, application of Load Matrix to a heavy-duty diesel engine is presented.

An existing pass by noise data acquisition system was upgraded to provide the sophisticated data analysis techniques and test site efficiency required to comply with the current and future drive by noise regulations. Use of six sigma tool such as voice of the customer helped in defining the customer requirements which were then translated into the desired engineering characteristics using QFD. Pugh concept matrix narrowed down the best option suitable for the test site modifications taking into account the critical constraints such as test complexity, system cost & transparency to the existing drive by noise setup. Features of the new system include data telemetry, frequency analysis, portability and efficient data management through the use of advanced data acquisition system. Wireless mode of the data transmission helped significantly avoid most of the test site modifications, which in turn helped to reduce the overall system implementation cost.

Engine noise is one of the significant aspects of product quality for light and medium duty diesel engine market applications. Gear whine is one of those noise issues, which is considered objectionable and impacts the customer’s perception of the product quality. Gear whine could result due to defects in the gear manufacturing process and/or due to inaccurate design of the gear macro and micro geometry. The focus of this technical paper is to discuss gear whine considerations from the production plant perspective. This includes quick overview of the measurement process, test cell environment, noise acceptance criteria considerations. A gear whine case study is presented based on the data collected in the test cell at the engine plant. Gear whine data acquired on current product and next generation of prototype engines is analyzed and presented. This paper concludes by highlighting the lessons learned from the case study.